Product Name

Unit

 Test Method

Condition

S706

S9000EP

Modified Categories

——

——

——

Glass Fiber Reinforced ABS

Flame RetardantABS

1. Density

g/cm³

ISO 1183

Dry

1.28

1.21

2. 24H Water Absorb(23℃，50%Relative Humidity)

%

ISO 62

3. Saturated Water Absorption（In water）

%

ISO 62

 Mechanical Properties

4.Tensile Stress

MPa

ISO 527

Dry/Wet

90/-

50/-

5. Elongation at Break

%

ISO 527

Dry/Wet

2/-

2/-

6. Flexural Stress

MPa

ISO 178

Dry/Wet

115/-

80/-

7. Flexural Modulus

MPa

ISO 178

 Dry/Wet

6400/-

3000/-

8. Notched Izod Impact Strength

KJ/m²

ISO 180

Dry/Wet

6.8/-

6.0/-

9. Hardness Rockwell

R

ISO 2039/2

Dry/Wet

110/-

110/-

  Thermal Properties

10. Heat Deflection Temperature (0.45MPa)

℃

ISO 75

110

87

Heat Deflection Temperature (1.80MPa)

℃

ISO 75

101

75

11.  Linear Therma Expansion

10^-5/K

ASTM D696

Dry/Wet

12. Injection Molding Temperature

℃

195/245

190-235

13. Linear Molding Shrinkage (flow diretion)

%

Dry

14. Melt Flow Rate

g/10min

ISO 1133

Dry

15. Mold Temperature

℃

40-50

40-50

16. Melt Point

℃

DSC法

160

160

 Electrical Properties

17. Surface Resistivity

Ω

ASTM D257

Dry/Wet

10¹⁶/-

10¹⁵/-

18. Dielectric Strength

KV/mm

ASTM D149

Dry/Wet

16/-

18/-

19. Fire Retardant Rating(1/16 inch)

UL-94

HB

V-0

20. Use 

Electrical Devices

Fire-proof Household Appliances